I te mea ko te Alumina ceramic wafer oro me te sapphire lapping kōpae whakamahia i roto i te āhua-conductive, taimana oro etc.
Tukatuka: Nga momo katoa o te whakakorikori me te mahi mirimiri, penei i te CMP matū miihini whakakorikori, Miihini Miihini, Miihini Miihini.
Te parakore teitei me te mauroa matū
Te Kaha Miihini Teitei me te Maamaa
Atete Te Waikura Nui
Atete Ngaohiko Teitei
Te Paemahana Teitei ki te 1700ºC
Tino Abrasion Atete Mahi
Mahinga Mahinga Pai
Nga momo Rahi katoa 180,360, 450, 600mm etc
ingoa hua | 99.7 parakore teitei Alumina uku oro Kōpae tukituki |
Rauemi | 99.7% alumina |
Rahi Pūnoa | D180, 360, 450, 600mm, kua whakaaetia te rahi. |
Tae | Rei rei |
Taupānga | Wafer me Sapphire CMP tukanga i roto i te ahumahi āhua-conductive |
Min.Ota | 1Pic |
Waeine | 99.7 Konumina Ceramic | ||
Nga Tikanga Whanui | ihirangi Al2O3 | Wt% | 99.7-99.9 |
Kiato | gm/cc | 3.94-3.97 | |
Tae | - | Rei rei | |
Te whakauru wai | % | 0 | |
Nga Taonga Miihini | Te Kaha Toka(MOR) 20 ºC | Mpa(psix10^3) | 440-550 |
Kōwae Elastic 20ºC | GPa (psix10^6) | 375 | |
Vickers Te pakeke | Gpa(kg/mm2) R45N | >=17 | |
Te kaha piko | Gpa | 390 | |
Te Kaha Maama 25ºC | MPa(psix10^3) | 248 | |
Maamaa Whati (KI c) | Mpa* m^1/2 | 4-5 | |
Nga Taonga Ngawha | Waawera te kawe (20ºC) | W/mk | 30 |
Te whakarea o te roha Ngawha(25-1000ºC) | 1x 10^-6/ºC | 7.6 | |
Te Atete Ngaaariki | ºC | 200 | |
Te pāmahana whakamahi mōrahi | ºC | 1700 | |
Nga Taonga Hiko | Kaha Dielectric (1MHz) | ac-kv/mm(ac v/mil) | 8.7 |
Dielectric Tonu(1 MHz) | 25ºC | 9.7 | |
Rōrahi ātete | ohm-cm (25ºC) | >10^14 | |
ohm-cm (500ºC) | 2×10^12 | ||
ohm-cm (1000ºC) | 2×10^7 |